Evaluation of Microstructure and Mechanical Property of Inconel 600 Degraded under High Temperature
고온 열화된 Inconel 600강의 미세조직 및 기계적 특성 평가
정광후;김성종;
Jung, Kwang-Hu;Kim, Seong-Jong;
목포해양대학교 기관시스템공학부;
Division of Marine Engineering, Mokpo National Maritime University;
DOI : 10.5695/JKISE.2017.50.6.492
Abstract
In this study, we investigated the effect of thermal aging on mechanical characteristics of Inconel 600 nickel-based alloy. The thermal aging was conducted up to 1000 hours at an atmosphere of $650^{circ}C$. The microstructure of thermally aged specimens was investigated by an optical microscope (OM), scanning electron microscope (SEM) and energy dispersive spectrometer (EDS). In addition, tensile test (strain rate: 2 mm/min) and micro Vickers hardness test were conducted to evaluate mechanical properties with time. As a result of the experiment, Cr-rich carbide continuously precipitated during thermal aging, leading to the change of the mechanical characteristics and fracture mode. With the increase of aging time, tensile strength, yield strength, and hardness gradually decreased. The fracture mode changed from ductile to brittle with the increase of grain boundary carbide.
Keywords
Inconel 600;High-temperature;Degradation;Microstructure;Mechanical property;
PDF